无限视频高清在线观看免费_成人毛片免费在线_女人15一17毛片_抽插丰满内射高潮视频_免费观看又黄又爽的视频_久操久操久操_色欧美色美色一区二区在线_成 人 免费 黄 色_综合网日日天干夜夜久久_中日韩一卡二卡三卡四_日本欧美视频_中日AV高清字幕版在线观看_国产国语av_日本高清不卡中文字幕免费_国产综合图_久久国产精品久久精品_欧美 日韩 亚洲 一区_久久精品国产亚洲AV麻豆～_激情亚洲图片激情亚洲小说_国产69精品久久久久99_国产毛片欧美毛片久久久_久中文字幕一区_国内国外日产一区二区_97涩涩涩_三及片免费看_国产成人免费ā片在线观看_日韩城人在线_亚洲爆乳精品无码一区二区三区_精品免费观看_玩丰满女领导对白露脸视频

What are the requirements for raw materials in cold heading machines

1. The chemical composition and mechanical properties of the raw materials used for cold heading in the cold heading machine should comply with the relevant standards for multi station automatic cold heading machines.

2. The raw material must undergo spheroidization annealing treatment, and its metallographic structure is spherical pearlite level 4-6.

3. In order to minimize the tendency of cracking and improve the service life of the mold, the hardness of the raw materials needs to be as low as possible for the cold drawn materials to increase plasticity. Generally, the hardness of raw materials is required to be between HB110 and 170 (HRB62-88).

4. The dimensional accuracy of cold drawn materials should generally be determined according to the specific requirements and process conditions of the product. Multi station cold heading machines generally have lower requirements for the precision of reduced diameter and strong reduction dimensions.

5. The surface quality of cold drawn materials requires a lubricating film with a dull dark color, and the surface must not have defects such as scratches, folds, cracks, burrs, rust, oxide scales, pits, and pitting.

6. It is required that the total thickness of the decarburization layer in the radial direction of the cold drawn material should not exceed 1-1.5% of the diameter of the raw material (the specific situation depends on the requirements of each manufacturer).

To ensure the cutting quality during cold forming, it is required that the cold drawn material has a hard surface and a soft core.

8. Cold drawn materials should undergo cold forging tests. Wenzhou cold heading machines also require materials to have lower sensitivity to cold work hardening, in order to reduce the increase in deformation resistance caused by cold work hardening during the deformation process.